1. Abstract : during construction of the capital international airport ' s garage building project , the c50 and over c60 high performance concrete has been adopted for its construction . for the aim of 1 , to get a maximum reduction of cement comsumption 2 , to lower the concrete ' s hydration heat 3 , to reduce concrete ' s shrinkage and cracks , and 4 , to promote concrete ' s performance , a high quality chilled blast furnace superfine slag has been adopted as an admixture . furthermore , the adoption of some other minerals as the admixtures to get a high performance concrete has been carried out . as a result , these procedures and operations would have developed considerably the potential activity of concrete , and eventually the multiple performance and multiple function of concrete would have been improved and promoted . in conclusion a good result has been achieved in practice
   文摘:首都国际机场停车楼工程中，采用c50及c60以上高性能混凝土，为最大限度减少水泥用量，降低水化热，减少收缩与裂缝，提高混凝土的性能，优选了有效成分含量高、质量好的水淬高炉矿渣磨细后单独掺用，或再与其他矿物组分复合作为高性能混凝土的掺合料，以充分发挥矿渣的潜在活性，从而使混凝土的多项性能得到极大的改善和提高，并在实际应用中取得了良好的效果。
2. During construction of the capital international airport ' s garage building project , the c50 and over c60 high performance concrete has been adopted for its construction . for the aim of 1 , to get a maximum reduction of cement comsumption 2 , to lower the concrete ' s hydration heat 3 , to reduce concrete ' s shrinkage and cracks , and 4 , to promote concrete ' s performance , a high quality chilled blast furnace superfine slag has been adopted as an admixture . furthermore , the adoption of some other minerals as the admixtures to get a high performance concrete has been carried out . as a result , these procedures and operations would have developed considerably the potential activity of concrete , and eventually the multiple performance and multiple function of concrete would have been improved and promoted . in conclusion a good result has been achieved in practice
   首都国际机场停车楼工程中，采用c50及c60以上高性能混凝土，为最大限度减少水泥用量，降低水化热，减少收缩与裂缝，提高混凝土的性能，优选了有效成分含量高、质量好的水淬高炉矿渣磨细后单独掺用，或再与其他矿物组分复合作为高性能混凝土的掺合料，以充分发挥矿渣的潜在活性，从而使混凝土的多项性能得到极大的改善和提高，并在实际应用中取得了良好的效果。